AISI 4140 Steel Bar, Steel Plate, Flats Supplier, Stockist and Exporter. AISI SAE 4140 alloy steel is a chromium molybdenum alloy steel specification widely used in general purpose high tensile steel for components, like axles, shafts, bolts, gears and other applications. Similar to alloy grade AISI 4130 chrome moly alloy steel but with a slightly higher carbon content. The higher carbon content of AISI 4140 steel gives greater strength and heat treatment capabilities in comparison to AISI / ASTM 4130 alloy steels, however it does have inferior weldability characteristics.
1. Supply Range for AISI alloy 4140 steel bar
4140 Steel Round Bar: diameter 8mm – 3000mm
4140 Steel Plate: thickness 10mm – 1500mm x width 200mm – 3000mm
4140 Steel Grade Square: 20mm – 500mm
Surface Finish: Black, Rough Machined, Turned or as per given requirements.
2. Common 4140 Steel Specifications
| Country | USA | German | British | Japan | China | Australia |
| Standard | ASTM A29 | DIN 17200 | BS 970 | JIS G4105 | GB/T 3077 | AS 1444 |
| Grades | 4140 | 1.7225/ 42CrMo4 |
42CrMo4 | SCM440 | 42CrMo | 4140 |
3. 4140 Steel Bar Chemical Composition
| Standard | Grade | C | Mn | P | S | Si | Cr | Mo |
| ASTM A29 | 4140 | 0.38-0.43 | 0.75-1.00 | 0.035 | 0.040 | 0.15-0.35 | 0.8-1.10 | 0.15-0.25 |
| EN 10083/EN 10250 | 42CrMo4/1.7225 | 0.38-0.45 | 0.6-0.9 | 0.035 | 0.035 | 0.4 | 0.9-1.2 | 0.15-0.30 |
| JIS G4105 | SCM440 | 0.38-0.43 | 0.60-0.85 | 0.03 | 0.03 | 0.15-0.35 | 0.9-1.2 | 0.15-0.30 |
4. Mechanical Properties of AISI Alloy 4140 Steel Bar, Plates, Square
| Properties | Metric | Imperial |
| Tensile strength | 655 MPa | 95000 psi |
| Yield strength | 415 MPa | 60200 psi |
| Bulk modulus (typical for steel) | 140 GPa | 20300 ksi |
| Shear modulus (typical for steel) | 80 GPa | 11600 ksi |
| Elastic modulus | 190-210 GPa | 27557-30458 ksi |
| Poisson’s ratio | 0.27-0.30 | 0.27-0.30 |
| Elongation at break (in 50 mm) | 25.70% | 25.70% |
| Hardness, Brinell | 197 | 197 |
| Hardness, Knoop (converted from Brinell hardness) | 219 | 219 |
| Hardness, Rockwell B (converted from Brinell hardness) | 92 | 92 |
| Hardness, Rockwell C (converted from Brinell hardness. Value below normal HRC range, for comparison purposes only) | 13 | 13 |
| Hardness, Vickers (converted from Brinell hardness) | 207 | 207 |
| Machinability (based on AISI 1212 as 100 machinability) | 65 | 65 |
5. Forging
Preheat the steel carefully, heat to 1150 oC – 1200 oC maximum, hold until temperature is uniform throughout the section.
Do not forge below 850 oC.Following forging operation the work piece should be cooled as slowly as possible.
6. AISI 4140 Steel Grade Heat Treatment
- Annealing
Heat ASTM 4140 steels to 800 oC – 850 oC, hold until temperature is uniform throughout the section and cool in furnace. - Normalizing
Heat steel alloy 4140 to 870 oC – 900 oC, hold until temperature is uniform throughout the section, soak for 10 – 15 minutes and cool in still air. - Tempering
Re-heat 4140 grade steel to 550 oC – 700 oC as required, hold until temperature is uniform throughout the section, soak for 1 hour per 25 mm of section, and cool in still air.
7. Hardening of AISI Alloy Steel 4140
AISI alloy 4140 steel bar, plate and square can be hardened by cold working, or heating and quenching.
SAE 4140 alloy steel is usually supplied ready heat treated to hardness in 18-22 HRC. If further heat treatment is required, then heat to 840 oC – 875 oC, hold until temperature is uniform throughout the section, soak for 10 – 15 minutes per 25 mm section, and quench in oil, water, or polymer as required.
8. Application of AISI alloy round 4140 steel bar
ASTM alloy 4140 steel bar, flat or plate material can be used for as wide variety of applications where greater toughness and wear resistance is needed over lower carbon grades. Typical applications for 4140 tool steel uses include Components, Adapters, Arbors,strippers, holder blocks, mold bases, ejectors, back up and support tooling, fixtures, jigs, molds, cams, drill collars, Axle Shafts, Bolts, Crankshafts,stubs, couplings, reamer bodies, axles, shafting, piston rods, rams, hydraulic machinery shafts, gears, sprockets, gear racks, chain links, spindles, tool bodies, tool holders, tie rods, Connection Rods, Chuck Bodies, Collets, Conveyor Pins & Rolls, Ejector Pins, Forks, Gears, Guide Rods, Hydraulic Shafts & Parts,Lathe Spindles, Logging Parts, Milling Spindles, Motor Shafts, Nuts, Pinch Bars, Pinions, Pump Shafts,boring bars,tracks, slides, wear strips or parts, forming dies, brake dies, trim dies, bolsters, machinery parts and components, etc.
Welcome customers to inquiry AISI 4140 steel bar, plate, flat steel for the 4140 steel price. We are professional supplier and exporter for more than 20 years. We offer you worldwide solution for aisi alloy 4140 steel bar.
9. Our Customers